Effect Of Surface Nanocrystallization Pretreatment On The Tribological Properties Of Plasma Nitrided Aisi 316 L Stainless Steel Under Boundary Lubrication

It has been proved that surface nanocrstallization pretreatment is beneficial to plasma nitriding of steel by enhancing nitrogen diffusion, while the tribological properties of the nitrided nanostructured steel under boundary lubrication are not clear. In this work, AISI 316 L stainless steel with and without ultrasonic cold forging technology (UCFT) pretreatment was plasma nitrided at 500 degrees C for 4 h. The effects of UCFT pretreatment on the microstructure and properties of the nitrided layer and the tribochemical interactions between the nitrided layer and friction modifier molybdenum dithiocarbamate (MoDTC) and antiwear additive zinc dialkyldithio-phosphate (ZDDP) were investigated using SRV tribometer, scanning electron microscopy (SEM), vickers hardness tester, optical microscope, X-ray diffraction, and X-ray photoelectron spectroscopy (XPS). Surface analyses confirm the formation of a 20 mu m thick nitrided layer on the UCFT-pretreated sample and it had higher hardness than that on the unpretreated sample. Furthermore, the nitrided UCFT-pretreated sample presented better synergetic effect with MoDTC and ZDDP on tribological behaviors than the nitrided unpretreated sample. This is attributed to the higher contents of Mo, S, Zn, P, and MoS2/MoO3 ratio in the tribofilms on the nitrided UCFT-pretreated sample.