Sol-gel route to highly transparent (Ho0.05Y0.95)2Ti2O7 thin films for active optical components operating at 2 μm
Optical Materials(2018)
Abstract
We present a generic sol-gel route to the preparation of optically active nanocrystalline holmium-yttrium titanate (Ho0.05Y0.95)2Ti2O7 thin films, which exhibit a strong luminescence at 2 μm. The films were prepared by the sol-gel process and thermally treated in a rapid thermal annealing furnace. The nanocrystal size and optical properties were tailored by the processing temperature. The final film thickness was around 500 nm. X-ray diffraction analysis and Raman spectroscopy confirmed the high purity of the crystal phase of (Ho0.05Y0.95)2Ti2O7. The activation energy of crystal growth was 35.7 kJ mol−1. The films had excellent structural and surface homogeneity causing their high transparency close to the theoretical limit of 93.39%. Refractive index of the film heat-treated at 1000 °C was around 1.98. The films exhibited strong emission at 2 μm with a luminescence lifetime around 4.6 ms. Their properties together with processing feasibility make them promising materials for photonic applications.
MoreTranslated text
Key words
Thin films,Rare earth compounds,Waveguide,Phosphor
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined