Thermal Annealing And Single-Domain Preparation In Tetragonal Pb(In1/2nb1/2)O-3-Pb(Mg1/3nb2/3)O-3-Pbtio3 Crystal For Electro-Optic And Non-Linear Optical Applications

The relaxor-PbTiO3 single crystal has attracted extensive attention in ultrasound transducers, sensors, actuators, and optoelectronics devices due to its excellent piezoelectric response and electro-optic properties. Preparation of a single-domain crystal as a critical process for application in electro-optic and non-linear optical devices suffers from serious and inevitable cracking. Therefore, a pre-poling thermal annealing process was suggested to release residual stress from crystal growth and the ferroelectric-paraelectric phase transition, which significantly reduced the chance of cracking. The effect of thermal annealing on dielectric properties, strain behavior, and domain structure were investigated. As a result, a significant increase of the dielectric constant near room temperature was obtained after annealing, which is close to the dielectric constant of the a-oriented domain. The annealed single crystal showed a lower and sharper strain peak at the coercive electric field compared with the unannealed sample, and the 90 degrees domain walls completely vanished, which was verified by optical microscopy. The crack-free single-domain crystal showed excellent optical quality, with high transmittance of approximately 70% in the visible and near-infrared regions, which indicates that this crystal is a promising candidate for applications in electro-optic and non-linear optical devices. Published by AIP Publishing.