SrZrO3 Formation at the Interlayer/Electrolyte Interface during (La1-xSrx)1-δCo1-yFeyO3 Cathode Sintering
JOURNAL OF THE ELECTROCHEMICAL SOCIETY(2017)
Abstract
This work probes the formation of SrZrO3 at the SDC/YSZ interface (Sm doped ceria, SDC; Y stabilized zirconia, YSZ) during (La1-xSrx)(1-delta)Co1-yFeyO3 (LSCF) cathode sintering. SEM/EDS and grazing incidence X-ray diffraction results of annealed LSCF and YSZ samples reveal that even without physical contact between LSCF and YSZ, SrZrO3 was formed on the surface of YSZ, preferentially at the grain boundaries. It was suspected that the SrZrO3 formation is due to the Sr-containing gas species diffused through the pores of the SDC layer and reacted with the YSZ electrolyte. Computational thermodynamics was adopted to predict the gas species formed in air during sintering by using the La-Sr-Co-Fe-O-H thermodynamic database. Sr(OH)(2) is identified as the dominant Sr-containing gas species under the experimental conditions. In addition, it was found that A-site deficiency in LSCF could effectively suppress the SrZrO3 formation while a dense and pore-free SDC interlayer is required to totally block the SrZrO3 formation. Cell performance was significantly improved for a cell with a dense SDC interlayer fabricated by pulsed laser deposition, due to elimination of SrZrO3 formation and therefore reduced interfacial resistance. (C) The Author(s) 2017. Published by ECS. This is an open access article distributed under the terms of the Creative Commons Attribution 4.0 License (CC BY, http://creativecommons.org/licenses/by/4.0/), which permits unrestricted reuse of the work in any medium, provided the original work is properly cited. All rights reserved.
MoreTranslated text
Key words
Liquid Phase Sintering
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined