Structure, optical property, and photo-catalytic activity of solid-solution β-AgAl1−xGaxO2 under visible light
Materials Science in Semiconductor Processing(2016)
摘要
Visible-light responsive β-AgAl1−xGaxO2 photocatalysts were prepared through a sol-gel method combined with a cation exchange reaction. The samples were characterized by X-ray diffraction, scanning electron microscopy, UV–vis absorption spectrum, and photoluminescence spectrum. The results demonstrated that the solid-solution β-AgAl1-xGaxO2 with delafossite structure showed high crystallinity. The microparticles with smooth surface were polycrystal and had polyhedron crystal morphologies. The optical band gap of the β-AgAl1−xGaxO2 was modulated in the range of 2.31–2.70eV; meanwhile the photoluminescence spectra showed a red shift by varying the molar ratio of Ga/Al from 0.25 to 4 attributed to the decrease of band gap. The photo-catalytic degradation of methyl orange was studied under visible light irradiation (wavelength>420nm). The degradation process followed the first-order kinetics. The β-AgAl0.2Ga0.8O2 with the reaction rate of 0.0402min−1 showed the highest photo-catalytic activity. This might be resulted from the narrow band gap of 2.31eV for the β-AgAl0.2Ga0.8O2 which could utilize visible light efficiently to photo-generate electrons and holes. The β-AgAl1−xGaxO2 had potential applications in degrading organic dyes by using visible light efficiently.
更多查看译文
关键词
Solid solution,β-AgAl1−xGaxO2,Visible-light response,Photo-catalytic activity
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要