Carbon Dioxide As A Green Carbon Source For The Synthesis Of Carbon Cages Encapsulating Porous Silicon As High Performance Lithium-Ion Battery Anodes

Si/C composite is one of the most promising candidate materials for next-generation lithium-ion battery anodes. Herein, we demonstrate the novel structure of carbon cages encapsulating porous Si synthesized by the reaction between magnesium silicide (Mg2Si) and carbon dioxide (CO2) and subsequent acid washing. Benefitting from the in situ deposition through magnesiothermic reduction of CO2, the carbon cage seals the inner Si completely and shows higher graphitization than that obtained from the decomposition of acetylene. After removing MgO, pores are created, which can accommodate the volume change of the Si anode during the charge/discharge process. As the anode material for lithium-ion batteries, the porous Si/C electrode shows a charge capacity of similar to 1124 mA h g(-1) after 100 cycles with 86.4% capacity retention at the current density of 0.4 A g(-1). When the current density increases to 1.6 and 3.2 A g(-1), the capacity can still be maintained at similar to 860 and similar to 460 mA h g(-1), respectively. The prominent cycling and rate performance is contributed by the built-in space for Si expansion, static carbon cages that prevent penetration of electrolyte and stabilize the solid electrolyte interface (SEI) outside, and fast charge transport by the novel structure.