Influence Of Calcium Chloride Impregnation On The Thermal And High-Temperature Carbonization Properties Of Bamboo Fiber

In this study, bamboo fiber was pretreated with calcium chloride (CaCl2) solution by using an ultrasonic method, and then heat-treated at 250 degrees C and carbonized at 1000 degrees C. The effect of impregnation with CaCl2 on the thermal and chemical properties and morphology of bamboo fiber was determined using thermogravimetric and differential thermogravimetric analyses, in situ Fourier transform infrared spectroscopy, and scanning electron microscopy. The pore structure of the carbonized bamboo fiber was investigated. The results revealed that bamboo fiber pretreated with 5% CaCl2 (BFCa5) showed a downward shift in the temperature of the maximum rate of weight loss253 degrees C and increase in char residue to 31.89%. BFCa5 was expected to undergo dehydration under the combined effect of oxygen-rich atmosphere and CaCl2 catalysis from 210 degrees C, and cellulose decomposition would be remarkable at 250 degrees C. Pretreatment with 5% CaCl2 promoted the formation of porous structure of the carbonized fiber, which exhibited a typical Type-IV isotherm, with the Brunauer-Emmett-Teller specific surface area of 331.32 m(2)/g an d Barrett-Joyner-Halenda adsorption average pore diameter of 13.6440 nm. Thus, CaCl2 was found to be an effective catalyst for the pyrolysis of bamboo fiber, facilitating the formation of porous carbonized fiber.