Revisiting the graphite nodule in ductile iron

The growth mechanism of graphite nodules in ductile iron was experimentally investigated using high-resolution 3D tomography of an individual graphite nodule in a near-eutectic ductile iron. The dual beam scanning electron microscopy (FIB-SEM) technique was used for this purpose. Iron particles elongated in the radial direction were observed inside a graphite nodule. Some micro-voids were detected inside the nodule, mostly located at the end of the iron particles. These observations were compared with established theories about the growth of graphite nodules and iron entrapment/engulfment in between the graphite sectors during solidification of ductile iron.