Effect of Vacuum-Sintering Temperature on Magnetic and Mechanical Properties of TiC-TiN-Ni-Mo-C Cermets

The effect of vacuum-sintering temperature ( T vs ), ranging from 1390 °C to 1470 °C, on magnetic and mechanical properties of TiC-10TiN-30Ni-6Mo-4C (mol pct) cermet was investigated in the present article. Room-temperature (RT) magnetization and maximum susceptibility decreased with increasing T vs up to 1450 °C, and then increased. This was mainly attributed to the fact that Ti content in the Ni-based binder phase increased with increasing T vs up to 1450 °C, suppressing ferromagnetism of the Ni matrix. RT ferromagnetism disappeared at T vs ≥ 1430 °C. Transverse rupture strength (TRS) reached a peak value at T vs = 1430 °C, and hardness did not significantly vary with T vs .