Low-Temperature Fabrication Of Sputtered High-K Hfo2 Gate Dielectric For Flexible A-Igzo Thin Film Transistors

In this work, low temperature fabrication of a sputtered high-k HfO2 gate dielectric for flexible a-IGZO thin film transistors (TFTs) on polyimide substrates was investigated. The effects of Ar-pressure during the sputtering process and then especially the post-annealing treatments at low temperature (<= 200 degrees C) for HfO2 on reducing the density of defects in the bulk and on the surface were systematically studied. X-ray reflectivity, UV-vis and X-ray photoelectron spectroscopy, and micro-wave photoconductivity decay measurements were carried out and indicated that the high quality of optimized HfO2 film and its high dielectric properties contributed to the low concentration of structural defects and shallow localized defects such as oxygen vacancies. As a result, the well-structured HfO2 gate dielectric exhibited a high density of 9.7 g/cm(3), a high dielectric constant of 28.5, a wide optical bandgap of 4.75 eV, and relatively low leakage current. The corresponding flexible a-IGZO TFT on polyimide exhibited an optimal device performance with a saturation mobility of 10.3 cm(2) V-1 s(-1), an I-on/I-off ratio of 4.3 x 10(7), a SS value of 0.28 V dec(-1), and a threshold voltage (V-th) of 1.1 V, as well as favorable stability under NBS/PBS gate bias and bending stress. Published by AIP Publishing.