Microstructure Investigation of Cu-Ni Base Al 2 O 3 Nanocomposites: From Nanoparticles Synthesis to Consolidation
Metallurgical and Materials Transactions A-physical Metallurgy and Materials Science(2017)
Abstract
Different compositions of Cu-Ni/Al 2 O 3 nanocomposites were prepared by a chemical-based synthesis of co-formed oxides (CuO-NiO-Al 2 O 3 ) nanoparticles followed by selective hydrogen reduction of the Cu and Ni oxides and finally by consolidation into pellets. The synthesized composites with both phases (metallic and oxide) containing nanoparticles in the 5 to 60 nm range have been systematically produced. Micro- and nanoscale characterization techniques were extensively employed in all stages of the process. X-ray diffraction (XRD) and transmission electron microscopy (TEM) analyses have shown a heterogeneous distribution of chemical elements resulting in the formation of Cu- and Ni-rich nanoparticles containing Al 2 O 3 phase in a controlled low volume fraction, which later mostly dispersed between the metallic particle and, to a lesser extent, within metallic particles. After consolidation, under uniaxial pressure followed by sintering, the compacted nanocomposite observed in the transmission electron microscope (TEM) revealed that the Al 2 O 3 have been more homogeneously distributed as such: the majority of it at the newly formed grain boundaries of the consolidated pellet and a small part of it within the metallic Cu-Ni matrix. Microhardness measurements demonstrate that dispersion of Al 2 O 3 was successfully achieved as reinforcement phase, yielding up to 100 pct increase in hardness.
MoreTranslated text
Key words
Cu2O, Rietveld Analysis, Al2O3 Phase, Field Transmission Electron Microscopy Image, Consolidate Composite
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined