Generation and development of damage in double forged tungsten in different combined regimes of irradiation with extreme heat loads

Armour materials in fusion devices, especially in the region of divertor, are exposed to a continuous heat and particle load. In addition, several off-normal events can reach the material during a work session. Calculations show that the effects of plasma and heat during such events can lead to cracking, erosion and detachment of the armour material. On the other hand, mutual and combined influences of different kinds of heat and particle loads can lead to the amplification of defects or vice versa, to the mitigation of damages.