Synthesis and luminescent behavior of Dy:Y3Ga5O12 phosphor for UV induced white LEDs
Optik(2017)
摘要
The synthesis, X-ray diffraction (XRD) pattern, excitation spectrum, emission spectra and decay times were studied for the first time to our best knowledge. The Dy:Y3Ga5O12 (Dy:YGG) phosphors with Dy3+ ions concentration of 0.5%, 1%, 3%, 5% and 10% were prepared by sol-gel method. The XRD patterns show that the phosphors possess perfect YGG phase. The average particle size of the Dy:YGG phosphors was calculated to be about 40nm. The strongest excitation peak was 353nm, which is favorable to ultra violet (UV) induced white light-emitting diodes (LEDs). Three emission bands centered at 480nm, 580nm and 672nm could be observed under excitation of 353nm. The yellow-to-blue integrated intensity ratios (Y/B) were 1.4–1.7 for the Dy3+ ions concentrations from 0.5 to 5%. The optimum Dy3+ concentration is 3%, and the corresponding 1931 Commission International de I’Eclairage (CIE) coordinates is (x=0.37, y=0.38). The results show that Dy:YGG phosphors can be a good candidate for UV-excitation warm-yellowish-white LEDs.
更多查看译文
关键词
Dy:Y3Ga5O12,White LEDs,Sol-gel,Phosphors
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要