Morphological, thermo-mechanical, and thermal conductivity properties of halloysite nanotube-filled polypropylene nanocomposite foam

Studies about polypropylene nanocomposite foams are receiving attention because nanoparticles can change physical and mechanical properties, as well as improve foaming behavior in terms of homogeneous cell structure, cell density, and void fraction. In this research, the foaming behavior of polypropylene, polypropylene/long-chain branched polypropylene (LCBPP) 100/20 blend, and polypropylene/LCBPP/halloysite nanocomposites with 0.5 and 3 parts per hundred of resin (phr) is studied. The LCBPP was used to improve the rheological properties of polypropylene/LCBPP blend, namely the degree of strain-hardening. Transmission electron microscopy observation indicated that halloysite nanotube particles are well distributed in the matrix by aggregates. Subsequent foaming experiments were conducted using chemical blowing agent in injection-molding processing. Polypropylene foam exhibited high cell density and cell size as well as a collapsing effect, whereas the polypropylene/LCBPP blend showed a reduction of the void fraction and cell density compared to expanded polypropylene. Also, the blend showed reduction of the collapsing effect and increase of homogeneous cell size distribution. The introduction of a small amount of halloysite nanotube in the polypropylene/LCBPP blend improved the foaming behavior of the polypropylene, with a uniform cell structure distribution in the resultant foams. In addition, the cell density of the composite sample was higher than the polypropylene/LCBPP sample, having increased 82% and 136% for 0.5 and 3 phr of loaded halloysite nanotube, respectively. Furthermore, the presence of halloysite nanotube increased crystallization temperature (Tc) and slightly increased dynamic-mechanical properties measured by dynamic-mechanical thermal analysis. By increasing halloysite nanotube content to 3 phr, the insulating effect increased by 13% compared to polypropylene/LCBPP blend. For comparative purposes, the effect on foaming behavior of polypropylene/LCBPP was also investigated using talc microparticles.