Influence of the Processing Variables on the Microstructure Evolution of a Bainitic Carbide-Free Steel

New trends focused on achieving higher performance steels has led to a so-called 3rd Generation Advanced High Strength Steels (AHSS), in which the typical polygonal ferrite found in TRIP steels as a matrix phase is replaced by harder phases as Carbide-Free Bainite (CFB) and/or (tempered) martensite. Besides, large volume fractions of retained austenite (R.A.) with adequate stability are aimed for to improve the formability of the steels. Si containing steels are regarded as the most suitable to retard cementite formation and consequently reach high volume fractions of RA. In this work, CFB annealing schedules were applied to dilatometer samples of Fe-0.22C-2.0Mn-1.3Si. The overaging temperature TB was varied between 390 oC and 480 oC, and other processing variables investigated were the austenitizing temperature Taus, and the overaging holding time tB. The annealed samples analyzed with LOM, FEG-SEM, EBSD and X-ray diffraction techniques show that markedly different complex microstructures made up of bainite, ferrite, MA phase and retained austenite (R.A) are accomplished depending on the specific thermal cycle. These results are described in detail and discussed in relation to the dilatometry measurements.