Deposition of thin films using argon/acetylene atmospheric pressure plasma jet

Atmospheric pressure plasma jet was used to deposit polymer films from argon/air/acetylene mixture. Depending on the gas composition, three modes of operation were observed and characterized. The film deposited by a stationary jet had a circular shape with area (where thickness was almost constant) about the nozzle inner diameter. The deposition rate of stationary jet decreased with the time: a film of 2μm was obtained after the first two minutes, while in the next two minutes only 1.3μm film was deposited. The plasma polymers were characterized by infrared spectroscopy, where variety of CH and few CO bonds were detected. By using a linear displacement system, we obtained homogeneous deposition over a larger area with deposition rate of about 330nm/min, showing the potential of such plasma jet system for large-scale depositions.