Dielectric, Piezoelectric Enhancement and Photoluminescent Behavior in Low Temperature Sintered Pr-Modified Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 Ceramics
Journal of Electronic Materials(2018)
Abstract
Pristine and 0.04 wt.% Pr 6 O 11 substituted Ba 0.85 Ca 0.15 Zr 0.1 Ti 0.9 O 3 (BCZT) lead-free ceramics have been synthesized by the conventional solid-state reaction method at 1450 and 1300°C sintering temperatures, respectively. The synthesized compounds were characterized by their structural, microstructural, piezoelectric, dielectric and luminescent properties. Coexistence of tetragonal and orthorhombic phases was observed for both pure and Pr doped BCZT compounds. Higher piezoelectric coefficient ( d 33 ) ∼ 220 pC/N, maximum dielectric constant ( ɛ m ) ∼ 4204 and minimum dielectric loss (tan δ ) ∼ 0.025 were obtained for Pr doped compound as compared to 180 pC/N, 3353 and 0.034 values, respectively, for the undoped BCZT ceramics. Strong photoluminescence emission spectra consisting of blue (489 nm), green (530 nm) and red (602 nm) light emissions were observed in Pr doped compound. Our results demonstrate that Pr 6 O 11 addition in BCZT ceramics is helpful in increasing the electrical properties, inducing the luminescent effect and simultaneously reducing the sintering temperatures of BCZT. The results have been understood in the light of Pr 3+ ions occupying the Ti 4+ -sites.
MoreTranslated text
Key words
Lead-free piezoelectrics,dielectric properties,photoluminescence properties
AI Read Science
Must-Reading Tree
Example
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined