High temperature oxidation resistance of Ni-(5∼13)Co-(10∼16)Cr-(5∼9)W-5Al-(1∼1.5)Ti-(3∼6)Ta alloys
Metals and Materials International(2016)
摘要
The oxidation behavior of Ni-based superalloys was examined by cyclic oxidation tests at 850 and 1000 °C. The present study focused on the investigation of two newly developed and three commercial alloys (GTD-111, IN738LC, and CM247LC). The oxidation resistance of the superalloys were evaluated by the oxidation rate constants and the mass gains. The oxidation scales mainly consisted of outer Cr 2 O 3 and inner Al 2 O 3 layers at both temperatures, as well as oxides of minor elements such as TiO 2 , NiCr 2 O 4 , CrTaO 4 , HfO 2 , and TaO. The oxidation resistance of the alloys containing larger amounts of Al, W, and Ta and lower Mo and Ti concentrations was higher than those of the other alloys. The ranking of oxidation resistance for the alloys corresponded to the statistical prediction drawn from a response surface analysis. Furthermore, these alloys contained more Ta oxides, such as CrTaO 4 and TaO, suggesting that Ta oxides had an active role in improving the oxidation resistance.
更多查看译文
关键词
alloys,oxidation,X-ray diffraction,Ni-based superalloys,cyclic oxidation test
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要