Structural Transformations of Hydrolysates Obtained from Ti-, Zr-, and Ti, Zr-Solutions Used for Clay Pillaring: Towards Understanding of the Mixed Pillars Nature.

Structural characteristics of hydrolysates formed from the aqueous Ti-, Zr-, and Ti, Zr-pillaring solutions prepared from inorganic precursors (TiCl4 and ZrOCl2), was investigated and compared with that of precipitates obtained from the same solutions after a slight alkalization of pH to the values reported for the conditions of clay pillaring. The materials were recovered by lyophilization and subsequently subjected to calcination at 500, 800 and 1000 degrees C. Of special interest was the effect of pH on the possible formation of mixed Ti, Zr-oxide species. Powder X-ray diffraction (XRD), Raman spectroscopy and scanning electron microscope/energy dispersive spectrometer (SEM/EDS) analysis showed that even a relatively moderate alteration of pH in Ti-, Zr-, or Ti, Zr-precursor solutions caused substantial changes in the outcome of hydrolytic transformations, manifested by different phase and/or chemical composition of the resulting hydrolysates. Analysis of thermal evolution of hydrolysates showed that alkalization facilitated the transformation of anatase into rutile in materials obtained from Ti-pillaring solution, but retarded tetragonal to monoclinic zirconia conversion in samples derived from Zr-pillaring agent. The most striking effect was observed for the mixed Ti, Zr-pillaring solution, where an increase of pH enabled the formation of zirconium titanate as the only crystalline phase, rather than a multiphase mixture of anatase, monoclinic zirconia and zirconium titanate obtained from the more acidic precursor. The finding supports the model of mixed Ti-O-Zr network in props generated in Ti, Zr-pillared montmorillonites.