Influence Of Ag On The Properties Of Ca0.9yb0.1mno3 Sintered Ceramics

In this study, Ca0.9Yb0.1MnO3 + x wt.% Ag (with x = 0, 1, 3, 5, and 10) thermoelectric materials were prepared via the classical ceramic method. In spite of the very high sintering temperature (1300 degrees C), no significant Ag losses were observed following this process. Moreover, Ag addition enhanced cation mobility during sintering due to the formation of a liquid phase. Microstructurally, it was found that Ag decreases porosity; this was confirmed by density measurements. Ag was also found to promote the formation of a Ca2Mn2O5 secondary phase. Despite the presence of this secondary phase, samples with Ag displayed lower electrical resistivity than Ag-free ones, without a drastic decrease in the absolute Seebeck coefficient. The highest thermoelectric performances, which were determined by power factor, were obtained in 1 wt.% Ag samples. These maximum values are slightly higher than the best of those reported in the literature for sintered materials with similar compositions, with the additional advantage of their being obtained using a much shorter sintering procedure.