Competitive Adsorption of Carbon Monoxide and Water Vapour on MIL-100(Fe) Prepared Using a Microwave Method
ADSORPTION SCIENCE & TECHNOLOGY(2015)
摘要
Competitive adsorption of CO and water vapour on MIL-100(Fe) synthesized using a microwave method was systematically investigated. Adsorption equilibrium, kinetics of CO adsorption and the competitive adsorption of CO/H2O(V) within MIL-100(Fe) were evaluated. Results show that the unsaturated Fe(II) can enhance the adsorption amount of CO on MIL-100(Fe). The adsorbed amount of CO on MIL-100(Fe) was 2.56 mmol/g at 298 K and 10 bar with isosteric adsorption heat of 28.31-38.43 kJ/mol. MIL-100(Fe) had two kinds of adsorption sites with desorption activation energy of 53.38 and 109.5 kJ/mol for CO, respectively. The diffusion coefficient of CO through MIL-100(Fe) was approximately 2.85 times higher than that of water vapour (10.54 x 10(-16) cm(2)/s vs. 2.735 x 10(-16) cm(2)/s). The working adsorption amount of CO at 40% relative humidity was approximately 0.631 mmol/g, retaining 75% of the original adsorption amount, indicating that CO is more competitive than H2O on the surface of MIL-100(Fe) under humid conditions.
更多查看译文
关键词
competitive adsorption,microwave method,carbon monoxide
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要