Beam Diameter Dependence of Performance in Thick-Layer and High-Power Selective Laser Melting of Ti-6Al-4V.
MATERIALS(2018)
摘要
& nbsp; A 400 W high-power laser was used to fabricate 200-p.m-thick Ti-6Al-4V samples to evaluate the effects of small (50 p.m) and large (200 p.m) beam diameter on density, microstructure and mechanical properties. A series of single-track experiments demonstrated that it was challenging for the small-beam laser to fabricate smooth and defect-free scan tracks. A larger beam diameter efficiently avoided process instability and provided a more stable and uniform melt pool. By increasing the beam diameter, the density of multilayer samples reached 99.95% of the theoretical value, which is much higher than that achieved with the small beam diameter. However, it was difficult to completely eliminate defects due to serious spatter and evaporation. Moreover, all of the generated samples had relatively coarse surfaces. For the large beam diameter of 200 p.m, the optimal yield strength, ultimate tensile strength and elongation were 1150 MPa, 1200 MPa and 8.02%, respectively. In comparison, the small beam diameter of 50 p.m resulted in values of 1035 MPa, 1100 MPa and 5.91%, respectively. Overall, the large-diameter laser is more suitable for high-power selective laser melting (SLM) technology, especially for thick layers.
更多查看译文
关键词
selective laser melting,high layer thickness,high power,beam diameter,Ti6Al4V
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要