Effect of cross-linked chitosan iron (III) on vascular calcification in uremic rats.

Cross-linked chitosan iron (III) is a chitin-derived polymer with a chelating effect on phosphorus, but it is untested in vascular calcification. We evaluated this compound's ability to reduce hyperphosphatemia and its effect on vascular calcification in uremic rats using an adenine-based, phosphorus-rich diet for seven weeks. We used a control group to characterize the uremia. Uremic rats were divided according the treatment into chronic kidney disease, CKD-Ch-Fe(III)CL (CKD-Ch), CKD-calcium carbonate, or CKD-sevelamer groups. We measured creatinine, phosphorus, calcium, alkaline phosphatase, phosphorus excretion fraction, parathyroid hormone, and fibroblast growth factor 23. Vascular calcification was assessed using the aortic calcium content, and a semi-quantitative analysis was performed using Von Kossa and hematoxylin-eosin staining. At week seven, rats in the chronic kidney disease group had higher creatinine, phosphorus, phosphorus excretion fraction, calcium, alkaline phosphatase, fibroblast growth factor 23, and aortic calcium content than those in the Control group. Treatments with cross-linked chitosan iron (III) and calcium carbonate prevented phosphorus increase (20%-30% reduction). The aortic calcium content was lowered by 88% and 85% in the CKD-Ch and CKD-sevelamer groups, respectively. The prevalence of vascular changes was higher in the chronic kidney disease and CKD-calcium carbonate (62.5%) groups than in the CKD-Ch group (37.5%). In conclusion, cross-linked chitosan iron (III) had a phosphorus chelating effect similar to calcium carbonate already available for clinical use, and prevented calcium accumulation in the aorta.