Cellulose nanofibril film as a piezoelectric sensor material.
ACS applied materials & interfaces(2016)
摘要
Self-standing films (45-μm thick) of native cellulose nanofibrils (CNF) were synthesized and characterized for their piezoelectric response. The surface and the microstructure of the films were evaluated with image-based analysis and scanning electron microscopy (SEM). The measured dielectric properties of the films at 1 kHz and 9.97 GHz indicated a relative permittivity of 3.47 and 3.38 and loss tangent tan δ of 0.011 and 0.071, respectively. The films were used as functional sensing layers in piezoelectric sensors with corresponding sensitivities of 4.7 to 6.4 pC/N in ambient conditions. This piezoelectric response is expected to increase remarkably upon film polarization resulting from the alignment of the cellulose crystalline regions in the film. The CNF sensor characteristics were compared with those of polyvinylidene fluoride (PVDF) as reference piezoelectric polymer. Overall, the results suggest that CNF is a suitable precursor material for disposable piezoelectric sensors, actuator or energy generators with potential applications in the fields of electronics, sensors and biomedical diagnostics.
更多查看译文
关键词
cellulose nanofibrils,nanocellulose films,piezoelectric sensor materials,image-based analysis,relative permittivity,sensitivity measurement
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要