Effects of aromatic diacetylenes on polyurethane degradation by gamma irradiation

The effects of four aromatic diacetylenes on the gamma-irradiation-induced degradation of a commercial polyurethane were studied. Addition of 1 wt% of diphenylbutadiyne, which is homogeneously distributed in the polymer, effectively suppressed the polymer chain degradation. The dose required to decrease tensile strength by 50% was found to be 582 kGy for the polyurethane with 1 wt% of diphenylbutadiyne, while a dose of only 310 kGy for the polyurethane itself. The Young's modulus of the polyurethane alone decreased with dose; meanwhile the films with diphenylbutadiyne did not change. The films with p,p′-dinitrodiphenylbutadiyne behaved differently from others due to their inhomogeneous composition. The amide substituted diacetylenes also showed protecting effect, but in less extent due to the steric effect.