The fiber charge measurement depending on the poly-DADMAC accessibility to cellulose fibers

Cellulose fiber charge is a significant parameter for porous cellulose fibers, and strongly affects the swelling ability of cellulose fibers and the properties of cellulose-based materials as well. Actually, it includes surface charge and inner charge. The surface charge is mentioned often in papermaking wet-end chemistry, however, the inner charge or the total charge is paid less attention to. In this study, the cationic polydiallyldimethyl ammonium chloride (poly-DADMAC) with different molecular weight (Mw) was applied for the accessibility evaluation to the cellulose fiber charges by using polyelectrolyte adsorption technique. Results showed that higher fiber charge was detected by lower Mw poly-DADMAC (7.5–15 kDa) due to its highly efficient penetration into the fiber cell walls and neutralization with inner charges, while lower fiber charge was obtained by using higher Mw poly-DADMAC (higher than 100 kDa) because of its adsorption onto fiber surface. As a consequence, high-Mw poly-DADMAC was used to determine the surface charge of cellulose fibers, and low-Mw poly-DADMAC could be used to measure the total charge under the saturated adsorption and low ionic strength (or salts concentration). This was confirmed by SEM–EDS analysis. The low-Mw poly-DADMAC adsorption had a good agreement with conventional conductometric titration, and a linear regression equation with slope of 1.03 and regression coefficient of 0.99 was obtained.