Superhydrophobic Surface Prepared by Organic-Inorganic Hybrid Material on Plasma Spraying Al2O3+13wt. %TiO2 Ceramic Coating
Materials Science Forum(2015)
摘要
The plasma spraying Al2O3+13wt. %TiO2 ceramic coating was coated with organic-inorganic hybrid emulsion. The hybrid emulsion prepared through co-hydrolysis and copolycondensation reactions of tetraethoxysilane (TEOS) and methyltriethoxysilane (MTES), and methylsilicone resin was added in the emulsion to improve the film-forming properties. The morphologies, chemical compositions and hydrophobicity of the resulting surfaces were analyzed by scanning electron microscopy (SEM), 3-dimensional stereoscopic microscope, energy dispersive X-ray detector (EDX), Fourier transfer infrared spectrometer (FT-IR) and water contact angle measurement. When the mole ratio of TEOS/MTES and the weight ratio of methylsilicone resin were 1:1 and 3.5wt. %, respectively, this surface displayed good film-forming properties. The contact angle was 130.24°, and the contact angle hysteresis was less than 10°.
更多查看译文
关键词
sol gel process,superhydrophobic
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要