Effect of Ni/Sn ratio on martensitic transformation and magnetic properties in high‐Mn content Mn2Ni1.64−xSn0.36+x ferromagnetic shape memory alloys
PHYSICA STATUS SOLIDI A-APPLICATIONS AND MATERIALS SCIENCE(2015)
摘要
The effect of variation in Ni/Sn ratio on martensitic transformation (MT) and magnetic properties was investigated in high-Mn content Mn2Ni1.64-xSn0.36+x alloys. With the increase of Sn content, the MT temperature shifts substantially towards lower temperature, while the Curie temperature of austenite remains almost unchanged. The reverse MT temperature decreases from 268 to around 80K for Mn2Ni1.64-xSn0.36+x alloys as x increases from 0.02 to 0.08. Under the low field of 1.2 T, the peak values of magnetic entropy changes are 9.8 J/kg K, 10.1 J/kg K, 10.3 J/kg K, and 6.1 J/kg K for x = 0.02, 0.04, 0.06, and 0.08, respectively. The abrupt changes in magnetization around MT temperatures and the field-induced metamagnetism should account for the large magnetic entropy changes. Incorporating the advantages of inexpensive and non-toxic raw materials, these high-Mn content alloys exhibit very promising prospects for the applications in magnetic refrigeration. (C) 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
更多查看译文
关键词
ferromagnetic materials,magnetocaloric effects,manganese,martensitic transformations,MnNiSn,shape memory alloys
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要