Synthesis of Fine MoSi 2 –Si 3 N 4 Composite Powders
Powder Metallurgy and Metal Ceramics(2023)
摘要
The features peculiar to the solid-state synthesis of MoSi 2 through vacuum heat treatment of a powder mixture of molybdenum and silicon nitride, as a precursor, in the temperature range 1000–1400°C were examined. X-ray diffraction established that the solid-state interaction began at 1100°C and progressed through the reaction diffusion of highly active silicon, resulting from the decomposition of Si 3 N 4 , into molybdenum to form lower Mo 3 Si and Mo 5 Si 3 silicide phases. In the temperature range 1100–1300°C, the redistribution of phases occurred: the contents of the starting molybdenum and β-Si 3 N 4 components in the reaction mixtures gradually decreased, while the contents of lower molybdenum silicides increased. Molybdenum disilicide formed in situ at 1400°C via successive development of lower silicide phases. The final product contained Mo 5 Si 3 . This was attributed to a deficiency of silicon as it evaporated at a temperature above 1200°C. This led to the conclusion that the addition of 20 wt.% excess silicon nitride was necessary to produce a homogeneous MoSi 2 phase and up to 40 wt.% excess silicon nitride to produce a two-phase MoSi 2 –Si 3 N 4 composite powder. The elevated temperature in the synthesis of MoSi 2 compared to conventional synthesis from simple elements was explained by the slow formation of active silicon in the Si 3 N 4 dissociation process. Based on the features observed in the solid-state vacuum interaction within the powder mixture of molybdenum and silicon nitride, as a precursor, a method was proposed for producing MoSi 2 –Si 3 N 4 composite powders, involving the introduction of 30 and 40 wt.% excess Si 3 N 4 powder. The synthesis resulted in agglomerated composite powders with a homogeneous distribution of the MoSi 2 and β -Si 3 N 4 phases. The MoSi 2 phase exhibited a capsular structure with a smooth surface. The synthesized composite powders are intended for the fabrication of components and parts with high oxidation resistance and corrosion resistance at elevated temperatures.
更多查看译文
关键词
solid-state synthesis,silicon nitride,molybdenum disilicide,composite powders,active silicon
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要