The Effects of Pre-strain and Subsequent Annealing on the Yielding Behavior in a Rolled Magnesium Alloy AZ31
Journal of Materials Engineering and Performance(2014)
摘要
In present work, pre-compression along the transverse direction and the normal direction (ND) was conducted on the rolled AZ31Mg alloy. Subsequently, the pre-compressed samples were annealed at 250 °C for different times. The effects of pre-compression and post-annealing on the yielding behavior during subsequent compression along ND were investigated. The results revealed that a lot of non-recrystallized extension twin remained in 5% PT sample after annealing for 4 h, while no twin was observed in the 5% PN sample, under the same annealing time. Along with, no prominent changes occurred in the texture of post-annealed as compared to pre-compressed samples. Due to the grain refinement caused by static recrystallization, yield strength increase of 5% PNA sample is found for an annealing time of 30 min. For the 5% PTA sample, the strength increase is attributed to annealing hardening (i.e., annealing retards the detwinning activity and consequently increase the yield strength).
更多查看译文
关键词
annealing hardening,magnesium alloy,twinning,yield strength
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要