Inassb Detectors For Visible To Mwir High Operating Temperature Applications

The Photon-Trap Structures for Quantum Advanced Detectors (PT-SQUAD) program requires MWIR detectors at 200 K. One of the ambitious requirements is to obtain high (>80 %) quantum efficiency over the visible to MWIR spectral range while maintaining high D* (> 1.0 x 10(11) cm root Hz/W) in the MWIR. A prime method to accomplish the goals is by reducing dark diffusion current in the detector via reducing the volume fill ratio (VFR) of the detector while optimizing absorption. Electromagnetic simulations show that an innovative architecture using pyramids as photon trapping structures provide a photon trapping mechanism by refractive-index-matching at the tapered air/semiconductor interface, thus minimizing the reflection and maximizing absorption to > 90 % over the entire visible to MWIR spectral range. InAsSb with bandgap appropriate to obtaining a cutoff wavelength similar to 4.3 mu m is chosen as the absorber layer. An added benefit of reducing VFR using pyramids is that no AR-coating is required.Compound-barrier (CB) detector test structures with alloy composition of the InAsSb absorber layer adjusted to achieve 200 K cutoff wavelength of 4.3 mu m (InAsSb lattice-matched to GaSb). Dark current density at 200 K is in the low 10-4 A/cm(2) at V-d = -1.0 V. External QE similar to 0.65 has been measured for detectors with a Si carrier wafer attached. Since illumination is through the Si carrier wafer that has a reflectance of similar to 30 %, this results in an internal QE > 0.9.