Salt-flux growth of HoCuMg4 single crystals
DALTON TRANSACTIONS(2023)
摘要
Polycrystalline samples of the magnesium-rich intermetallic compounds RECuMg4 (RE = Dy, Ho, Er, Tm) were synthesized by reaction of the elements in sealed tantalum ampoules heated in a high-frequency induction furnace. Phase purity of the RECuMg4 phases was ascertained by powder X-ray diffraction patterns. Well-shaped single crystals of HoCuMg4 could be grown in a NaCl/KCl salt flux and the crystal structure was refined from single crystal X-ray diffraction data: TbCuMg4 structure-type, space group Cmmm, a = 1361.4(2), b = 2039.3(4), c = 384.62(6) pm. The crystal structure of the RECuMg4 phases can be understood as a complex intergrowth variant of CsCl and AlB2 related slabs. The remarkable crystal chemical motif concerns the orthorhombically distorted bcc-like magnesium cubes with Mg-Mg distances ranging from 306 to 334 pm. At high temperatures DyCuMg4 and ErCuMg4 are Curie-Weiss paramagnets with paramagnetic Curie-Weiss temperatures of -15 K and -2 K for RE = Dy and Er, respectively. The effective magnetic moments, 10.66 mu(B) for RE = Dy and 9.65 mu(B) for RE = Er prove stable trivalent ground states for the rare earth cations. Magnetic susceptibility and heat capacity measurements reveal long-range antiferromagnetic ordering at low temperatures (<21 K). Whereas DyCuMg4 exhibits two subsequent antiferromagnetic transitions at T-N = 21 and 7.9 K which successively remove half of the entropy of a doublet crystal field ground state of Dy, ErCuMg4 shows a single, possibly broadened, antiferromagnetic transition at 8.6 K. The successive antiferromagnetic transitions are discussed with respect to magnetic frustration in the tetrameric units present in the crystal structure.
更多查看译文
关键词
hocumg4,single crystals,salt-flux
AI 理解论文
溯源树
样例
生成溯源树,研究论文发展脉络