The Reduction of TED in Ion Implanted Silicon

The leading challenge in the continued scaling of junctions made by ion implantation and annealing is the control of the undesired transient enhanced diffusion (TED) effect. Spike annealing has been used as a means to reduce this effect and has proven successful in previous nodes, The peak temperature in this process is typically 1050 degrees C and the time spent within 50 degrees C of the peak is of the order of 1.5 seconds. As technology advances along the future scaling roadmap, further reduction or elimination of the enhanced diffusion effect is necessary. We have shown that raising the peak. temperature to 1175 degrees C or more and reduction of the anneal time at peak temperature to less than a millisecond is effective in eliminating enhanced diffusion. We show that it is possible to employ a sequence of millisecond anneal followed by spike anneal to obtain profiles that do not exhibit gradient degradation at the junction and have junction depth and sheet resistance appropriate to the needs of future technology nodes. We have implemented millisecond annealing using a carbon dioxide laser to support high-volume manufacturing of 65 nm microprocessors and system-on-chip products. We further show how the use of molecular ion implantation to produce amorphousness followed by laser annealing to produce solid phase epitaxial regrowth results in junctions that meet die shallow depth and abruptness requirements of the 32 nm node.