Fabrication and properties of high performance YBa2Cu3O7−δ radio frequency SQUIDs with step-edge Josephson junctions

We describe the fabrication of high performance YBa2Cu3O7-delta (YBCO) radio frequency (RF) superconducting quantum interference devices (SQUIDs), which were prepared on 5 mm X 5 mm LaAlO3 (LAO) substrates by employing step-edge junctions (SEJs) and in flip-chip configuration with 12 mmX12 mm resonators. The step in the substrate was produced by Ar ion etching with step angles ranging from 47 degrees to 61 degrees, which is steep enough to ensure the formation of grain boundaries (GBs) at the step edges. The YBCO film was deposited using the pulsed laser deposition (PLD) technique with a film thickness half of the height of the substrate step. The inductance of the SQUID washer was designed to be about 157 pH. Under these circumstances, high performance YBCO RF SQUIDs were successfully fabricated with a typical flux-voltage transfer ratio of 83 mV/Phi(0), a white flux noise of 29 mu Phi(0)/root Hz, and the magnetic field sensitivity as high as 80 fT/root Hz. These devices have been applied in magnetocardiography and geological surveys.