Effect Of Strain On Ferroelectric Field Effect In Strongly Correlated Oxide Sm0.5nd0.5nio3

We report the effect of epitaxial strain on the magnitude and retention of the ferroelectric field effect in high quality PbZr0.3Ti0.7O3 (PZT)/3.8-4.3 nm Sm0.5Nd0.5NiO3 (SNNO) heterostructures grown on (001) LaAlO3 (LAO) and SrTiO3 (STO) substrates. For SNNO on LAO, which exhibits a first-order metal-insulator transition (MIT), switching the polarization of PZT induces a 10K shift in the transition temperature T-MI, with a maximum resistance change between the on and off states of Delta R/R-on similar to 75%. In sharp contrast, only up to 5% resistance change has been induced in SNNO on STO, where the MIT is second-order, with the modulation of T-MI negligibly small. We also observe thermally activated retention of the off state resistance R-off in both systems, with the activation energy of 22 meV (28 meV) for devices on LAO (STO). The time dynamics and thermal response of the field effect instability points to phonon-assisted interfacial trapping of charged mobile defects, which are attributed to strain induced oxygen vacancies. At room temperature, R-off stabilizes at similar to 55% and similar to 19% of the initial switching levels for SNNO on LAO and STO, respectively, reflecting the significantly different oxygen vacancy densities in these two systems. Our results reveal the critical role of strain in engineering and modeling the complex oxide composite structures for nanoelectronic and spintronic applications. (C) 2015 AIP Publishing LLC.