Study Of The Magnetoresistance Of Magnetic Film Modified By Using Ion Beams

We have studied the magnetoresistance (MR) of locally modified Cu(20 nm)/AlOx(1 nm)/NiFe (20 nm)/AlOx(1 nm)/Cu(3 nm) on a Si substrate. The local modification was performed by irradiating Cu ion beams on a photoresist wire-covered film. After irradiation, the hysteresis loop shows step-like behavior at a specific ion dose, which is caused by the difference in the switching fields of the irradiated and unirradiated region of the film. Because of this, plateau-like behavior is observed in the transverse MR measurement of the film with 1 x 10(16) ions/cm(2). A cross-sectional transmission electron microscopy image shows the irradiation induced intermixing of the magnetic layer with nonmagnetic layers. (C) 2011 American Institute of Physics. [doi:10.1063/1.3563070]