Study on Very-High-Cycle-Fatigue Property of Aero-Engine Blades Based on Subcomponent Specimen

The cyclic load number of aero-engine blade during its service life is very likely beyond 107, which is regarded as the conventional fatigue limit. Moreover, surface strengthening is very often used in the manufacturing process of blade. The conventional testing method in the VHCF regime cannot exactly reflect the stress state of the blade, including the mechanism of crack initiation. To study the fatigue behavior and effects of laser shock peening, a kind of bending fatigue subcomponent specimen was designed and the laser shock peening model was established. Experiment about TC17 was accomplished by the Ulra-High Cycle bending fatigue system. It is found that the fatigue damage occurs beneath the surface and the S-N curve is continuously rather than multi-step declining in the VHCF regime. Process of surface strengthening has a significant effect on fatigue performance of TC17 titanium alloy.