Preparation of NiO-YSZ Composite Powder Through 2-Step Hydrothermal Synthesis and Its Application to Solid Oxide Fuel Cell Anode Functional Layer

JOURNAL OF NANOSCIENCE AND NANOTECHNOLOGY(2015)

Cited 5|Views3
No score
Abstract
NiO-YSZ composite powders were prepared by 2-step hydrothermal synthesis and applied as an anode functional layer to improve the performance of SOFCs. The precursor solution containing yttrium chloride, zirconium oxychloride, and nickel nitrate was hydrothermally treated at 100 similar to 130 degrees C for 36 h and then calcined at 900 degrees C for 4 h. The results of X-ray diffraction, Field-Emission Scanning Electron Microscope and Transmission Electron Microscope showed that the NiO (50 similar to 100 nm) and YSZ (200 similar to 300 nm) were successfully synthesized and these two phases were well separated with the weak agglomeration. Electrical conductivity of the cermet made from the powders produced by 2-step hydrothermal synthesis was much higher than that of the cermet prepared by ball milling. A single cell with anode functional layer showed a maximum power density of 1.7 W/cm(2) at 800 degrees C, which may be owing to the homogeneous distribution and the small particle size of the obtained powders.
More
Translated text
Key words
NiO-YSZ,Hydrothermal Synthesis,Anode Functional Layer,Solid Oxide Fuel Cells
AI Read Science
Must-Reading Tree
Example
Generate MRT to find the research sequence of this paper
Chat Paper
Summary is being generated by the instructions you defined