Laser Cladding of MCrAlY Coatings on Stainless Steel

MCrAlY alloys (where M stands for Ni,Co or both) are commonly used as overlay protective coatings in gas turbine engine components against high temperature oxidation and corrosion. The protective effect of these alloys is due to the formation of a continuous thermally stable oxide layer on the coating surface. In this work several types of MCrAlY alloys, differing in their elemental composition, have been deposited on austenitic stainless steel by means of laser cladding. The microstructure of the coatings have been characterized by SEM-EDSand XRD. As expected, elemental composition compatible with γNi/γ’ Ni3Al,γNi/β-NiAl or γCo/β-(Co,Ni)Al phases are observed in hypoeutectic or hypereutectic microstructures depending on the alloy composition. The high temperature oxidation behavior of the coatings was evaluated by air furnace oxidation tests at 1100°C for 200h. The oxidized surface of the samples was examined by SEM-EDS and the oxides present identified by theoretical stoichiometric calculations. Results indicate the formation of a uniform Al3O2protective oxide scale with NiO,CoO, Y2O3/YAlO3 and Cr2O3 oxide inclusions.