Highly Water-Dispersible Surface-Modified Gd2o3 Nanoparticles For Potential Dual-Modal Bioimaging

Water-dispersible and luminescent gadolinium oxide (GO) nanoparticles (NPs) were designed and synthesized for potential dual-modal biological imaging. They were obtained by capping gadolinium oxide nanoparticles with a fluorescent glycol-based conjugated carboxylate (HL). The obtained nanoparticles (GO-L) show long-term colloidal stability and intense blue fluorescence. In addition, L can sensitize the luminescence of europium(III) through the so-called antenna effect. Thus, to extend the spectral ranges of emission, europium was introduced into L-modified gadolinium oxide nanoparticles. The obtained Eu-III-doped particles (Eu:GO-L) can provide visible red emission, which is more intensive than that without L capping. The average diameter of the monodisperse modified oxide cores is about 4nm. The average hydrodynamic diameter of the L-modified nanoparticles was estimated to be about 13nm. The nanoparticles show effective longitudinal water proton relaxivity. The relaxivity values obtained for GO-L and Eu:GO-L were r(1)=6.4 and 6.3s(-1)mM(-1) with r(2)/r(1) ratios close to unity at 1.4T. Longitudinal proton relaxivities of these nanoparticles are higher than those of positive contrast agents based on gadolinium complexes such as Gd-DOTA, which are commonly used for clinical magnetic resonance imaging. Moreover, these particles are suitable for cellular imaging and show good biocompatibility.