Synthesis, Characterization And Ferroelectric Properties Of Lead-Free K0.5na0.5nbo3 Nanotube Arrays

Lead-free K0.5Na0.5NbO3 (KNN) nanotube arrays were synthesized by a sol-gel method with anodic aluminum oxide templates. The obtained KNN nanotubes exhibited a polycrystalline and monoclinic perovskite structure with diameters of similar to 200 nm and wall thickness of similar to 30-40 nm, respectively. The polarization-electric loop curve of the nanotubes array were examined showing the values of 2P(r) and 2E(c) at about 3.4 mu C/cm(2) and 13 kV/cm, respectively, under a maximum electric field of 12.5 kV/cm. The piezoelectric characteristics of individual KNN nanotube array was also identified through piezoresponse force microscopy. (C) 2011 American Institute of Physics. [doi:10.1063/1.3592636]