Fabrication And Characterization Of La0.6sr0.4co0.2fe0.8o3-Delta-Yttria Stabilized Zirconia Composite Cathodes Prepared By Infiltration Method
ECS Transactions(2011)
摘要
Composite cathodes of yttria stabilized zirconia (YSZ) with Sr-, Co-doped LaFeO3 (LSCF) were prepared by infiltration of a porous YSZ matrix with different weight of aqueous solutions of the stoichiometric metal salts, followed by firing at various temperatures. X-ray diffraction measurements showed that the LSCF perovskite phase had formed at 800-900 degrees C and that solid-state reaction with the YSZ does not occur below approximately 950 degrees C. Various contents of LSCF from 15 wt% to 60 wt% are loaded in porous YSZ of anode supported cell (porous YSZ parallel to YSZ parallel to NiO-YSZ). The cell with 45 wt% LSCF exhibits better performance and lower interfacial resistance. The cell performance of LSCF fired at 850 degrees C is better than that of LSCF fired at 800 and 900 degrees C. The peak power densities of YSZ anode supported cell with 45 wt% LSCF fired at 850 degrees C are about 640, 869, and 972 mWcm(-2) at 700, 750, and 800 degrees C, respectively. The infiltrated LSCF cathode displays high catalytic activity and performance for the unique nano film coating fabricated with certain content at low temperature.
更多查看译文
关键词
null
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要