Behavior Of Coal-Based Direct Reduction Reaction Of Iron Oxide Pellets By Microwave Heating

The temperature rising characteristics and reaction of the reduction of iron oxide pellets with anthracite fines were studied using a MW-L0316V microwave oven and Leica-DM-RXP polarizing microscope. The results show that iron oxide pellets and anthracite fines have good microwave absorbing properties, and high temperature and reducing atmosphere in a relatively short time for reduction of iron oxide pellets can be achieved. The reduction reaction, which follows the unreacted core model, is rapid and the metallization increases from 13.41% to 56.57% as the reduction end point temperature increases from 850 degrees C to 950 degrees C. The iron is formed, fine grain crystals of iron are transferred and the contraction of metal phase occurs firstly at the surface of pellets, which hinders the reduction reaction at the center of pellets. The rate of reduction reaction increases slowly as the reduction end point temperature increases from 950 degrees C to 1050 degrees C.