Magnetic Field Dependence Of Voltage-Current Characteristics Of Fe3o4 Thin Films At Room Temperature
APPLIED PHYSICS LETTERS(2006)
摘要
Fe3O4 thin films have been fabricated on glass substrate by the facing-target sputtering technique and their field-modulated voltage-current behavior was investigated. The nonlinear dependence of voltage on current density displays a switching from high-resistivity to low-resistivity states above a threshold current density. The low-resistivity state is very sensitive to the applied magnetic field, and a large negative magnetoresistance of similar to-27% is observed at 300 Oe under a high current density of 100 A cm(-2) at room temperature. Furthermore, the dependence of the magnetoresistance on the magnetic field reveals a good linear relationship. The observed results seem to favor a picture of spin-polarized intergrain tunneling through the grain boundaries. (c) 2006 American Institute of Physics.
更多查看译文
关键词
null
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要