Violet-blue afterglow luminescence properties of non-doped SrZrO 3 material
Journal of Luminescence(2013)
摘要
Non-doped SrZrO3 material is synthesized by solid state reaction at 1300°C in air. The violet-blue afterglow luminescence of SrZrO3 centered at 395nm is firstly observed. The afterglow emission band (300–550nm) of SrZrO3 partly overlaps the absorption (200–400nm) of commercial photocatalyst TiO2 (P25). Thus, the SrZrO3 shows potential application to support photocatalytic activity of TiO2 even at night. The decay curve indicates that the afterglow luminescence of the present SrZrO3 can last less than 100s (0.32mcd/m2) and thus the present SrZrO3 still needs further improvement for practical application. The thermoluminescence indicates that at least two types of deep traps exist in the SrZrO3 and the depths of traps are roughly calculated to be as deep as 0.98eV and 1.76eV. It reveals that the short afterglow time of the SrZrO3 is not due to the lack of enough traps but the traps in SrZrO3 being too deep. Therefore, decreasing the depth of traps in SrZrO3 is our following emergency work.
更多查看译文
关键词
Luminescence,Optical materials,Optical properties
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要