Experimental Study On The Pulverization And Reduction Behavior Of Sinter In Oxygen Blast Furnace

Using the facility of reduction experiment, the low temperature reduction pulverization and reduction behavior of sinter in oxygen blast furnace (OBF) were studied. Through analyzing the results, the difference of pulverization and reduction behavior of sinter in OBF and conventional blast furnace (BF) were discussed. Furthermore, the effect laws of reduction temperature and the content of CO and H-2 on reduction behavior of sinter were studied. Also the controlling step of iron oxide reduction was discussed. Compared with BF, the low temperature reduction pulverization of sinter became serious at 773 K; reduction rate became faster at 1173 K; reduction time became less and final reduction degree was increased in OBF, With increasing of H-2 and CO contents, the reduction of sinter was promoted. The reduction process was controlled by interface chemical reaction at the earlier stage and by interface chemical reaction and internal diffusion at the final stage.