Examining of the segmented electrode use from the viewpoint of the electrolyte volatilizing in molten carbonate fuel cell

Molten carbonate fuel cells (MCFCs) have entered the pre-commercialization phase, and have been experimentally demonstrated in real world applications, including beer brewery, etc. However, though MCFCs have a high potential and an enough operating experience as an energy supply system, they are not explosively widespread. One of these reasons is cost of cell components. Because the thickness of both electrodes is 0.8mm and both electrodes are made of porous plates of 1m2 of the electrode area, they are often broken by a thermal stress in the sintering process of an electrode and by a worker's carelessness at the cell assembly process. Generally, because these cracking electrodes can potentially cause electrolyte leakage and gas crossover, they are not used to a MCFC stack and are disposed of. Therefore, it made the cost of MCFC be raised. The performance of a cell that uses a mosaic electrode has been evaluated. However, the causal relation between the cracking of an electrode and an electrolyte-leakage has not been yet confirmed. If this causal relationship is elucidated, a cracking electrode or a mosaic electrode can be used to MCFC, such that the cost of MCFC systems would consequently decrease. Therefore, we studied the causal relation between the cracking of an electrode and electrolyte leakage and gas crossover using a visualization technique. In the case of an anode electrode where the centre section of a cell has crack of about 1mm, the electrolyte leakage from this crack could not be observed by the visualization technique. Moreover, the gas crossover could not be also observed by the visualization technique, and nitrogen in the anode exhaust gas was not detected by a gas chromatography. However, the electrolyte leakage observed from the wet-seal section though the gap between the separator and the electrode was always 1mm or less. Therefore, electrolyte leakage hardly occurs, even if a cracked anode electrode is installed into the centre section of the cell. On the other hand, although the volatile substance gushes from the wet seal section, the electrolyte leakage/volatilization phenomenon does not occur at the centre of the cell or at the gap between each segmented cathode. The volatile substance in the cathode gas-distributor-channel is composed of the electrolyte mist and the electrolyte volatile substance, and the rate of release is about 2.5 times that of anode side. Although the segmented electrode can be applied to the anode in a MCFC, it cannot be applied to a cathode from the viewpoint of the electrolyte leakage/volatilization.