Identification and elimination of inductively coupled plasma-induced defects in Al _x Ga _{1- x} N/GaN heterostructures

By using temperature-dependent Hall,variable-frequency capacitance-voltage and cathodoluminescence (CL) measurements,the identification of inductively coupled plasma (ICP)-induced defect states around the Al x Ga 1-x N/GaN heterointerface and their elimination by subsequent annealing in Al x Ga 1-x N/GaN heterostructures are systematically investigated.The energy levels of interface states with activation energies in a range from 0.211 to 0.253 eV below the conduction band of GaN are observed.The interface state density after the ICP-etching process is as high as 2.75×10 12 cm 2 ·eV 1.The ICP-induced interface states could be reduced by two orders of magnitude by subsequent annealing in N 2 ambient.The CL studies indicate that the ICP-induced defects should be Ga-vacancy related.