New MgLi based Mg–Li–Cu–(Y, Gd) BMGs: Preparation, glass forming ability and mechanical properties
Journal of Non-Crystalline Solids(2011)
摘要
Through calculating the forming enthalpy by Modified Miedema Model, new MgLi-based bulk amorphous alloys Mg–Li–Cu–(Y, Gd) have been successfully designed and fabricated by conventional copper mold injection casting method. The X-ray diffractometer and differential scanning calorimeter results indicated that the as-cast Mg–Li–Cu–(Y, Gd) alloys were fully amorphous structure after casting to critical diameter as large as 4mm and 2mm. The experimental results also proved that with increasing Li content (3at.%–8at.%), the supercooled liquid region temperature of Mg–Li–Cu–(Y, Gd) alloys gradually decreased accompanying the reduce of glass forming ability. It was also found that appropriate addition of metal Li effectively increased the fracture strength and elastic strain and reduced their corresponding densities. The maximal fracture strength reached 468MPa and 478MPa, respectively, which were much higher than normal MgLi-based crystalline alloys (~300MPa).
更多查看译文
关键词
Bulk metallic glasses,,MgLi alloys,,Mechanical properties
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要