Synthesis and characterization of poly(ε-caprolactone) reinforced with aligned hybrid electrospun PMMA/nano-Al 2 O 3 fibre mats by film stacking
JOURNAL OF MATERIALS SCIENCE(2011)
摘要
PMMA and PMMA/10 wt% nano-Al 2 O 3 fibre mats were produced by means of electrospinning and used as reinforcing phase of poly(ε-caprolactone) matrix. The composite films were fabricated by means of film-stacking technique. SEM observations showed good wettability of PMMA-based fibres by the PCL matrix, confirming that a strong interface was formed. The Al 2 O 3 nanoparticles were well-distributed along the polymeric fibres. The introduction of PMMA fibres as a reinforcement led to a clear benefit in terms of the mechanical strength (11.5 ± 0.5 MPa), the value for neat PCL being 8.2 ± 2.2 MPa. The tensile strength was further increased when the fibres were loaded with nano-Al 2 O 3 (14.4 ± 0.6 MPa) due to both the presence of the ceramic filler and the smaller diameter of the composite fibres. A less marked improvement was instead found on stiffness.
更多查看译文
关键词
PMMA,Electrospun Fibre,Al2O3 Nanoparticles,Fibre Aspect Ratio,Composite Manufacturing
AI 理解论文
溯源树
样例
![](https://originalfileserver.aminer.cn/sys/aminer/pubs/mrt_preview.jpeg)
生成溯源树,研究论文发展脉络
Chat Paper
正在生成论文摘要